Stainless steels

STEEL CENTER SA

C%Si%Mn%P%S%Cr%Ni%N%
0,101,002,000,0450,15-0,351,70-19,08,0-10,00,11

Austenitic-antimagnetic stainless steel with a special composition that makes it suitable for use on automatic machines (revolvers). Used in the production of nuts, bolts, connectors, etc.

C%Si%Mn%P%S%Cr%Ni%N%
≤0,07≤1,00≤2,00≤0,045≤0,01517,5-19,58,00-10,5≤0,11

Austenitic-antimagnetic stainless steel providing protection against corrosion. Stainless steel products with this chemical composition are suitable for general use.

C%Si%Mn%P%S%Cr%Ni%N%
≤0,20≤1,50-2,50≤2,00≤0,045≤0,01519,0-21,011,0-13,0≤0,11

Austenitic-antimagnetic stainless steel with mechanical strength up to 1000 ° C. In terms of chemical resistance it can be used at: 1100 ° C in oxidizing atmosphere, 1050 ° C in oxidizing sulfite atmosphere, 900 ° C in reducing atmosphere.

C%Si%Mn%P%S%Cr%Ni%N%
≤0,10≤1,50≤2,00≤0,045≤0,01524,0-26,019,0-22,0≤0,11

Austenitic-antimagnetic stainless steel with excellent mechanical resistance to high temperatures (Refractory). Good tolerance to continuous temperature fluctuations even in noticeable abrupt thermal jumps. Restrictions on its use are: 1050 ° C in oxidizing atmosphere, 950 “C in oxidizing sulfite or reducing atmosphere, 750” C in reducing sulfur atmosphere.

C%Si%Mn%P%S%Cr%Mo%Ni%N%
≤0,17≤1,00≤2,00≤0,045≤0,01516,5-18,52,00-5,0010,00-13≤0,11

Austenitic-antimagnetic stainless steel with higher content of nickel, chromium and molybdenum. Provides augmented protection against corrosion

C%Si%Mn%P%S%Cr%Ni%T%
≤0,08≤1,00≤2,00≤0,045≤0,01517,0-19,09,00-12,0≤5xC

Austenitic-antimagnetic stainless steel with titanium that makes it highly resistant to intercrystalline corrosion even after welding. In addition, it is easily bondable and can be used even at temperatures of 700-800 C. Up to 200-300 “C retains its mechanical properties unchanged. The polish is moderate due to titanium

C%Si%Mn%P%S%Cr%T%
≤0,03≤1,00≤1,00≤0,04≤0,1510,5-12,5≤6x(C+N)

Ferritic-magnetic stainless steel with very good temperature resistance (Refractory).

C%Si%Mn%P%S%Cr%
≤0,25≤1,00≤1,50≤0,040≤0,01512,0-14,0

Ferritic-magnetic stainless steel used in the manufacture of molds, surgical instruments, knives, pump parts and machine components such as shafts, valves, etc. After proper heat treatment it can reach very high hardening levels. It has medium resistance to corrosion.

C%Si%Mn%P%S%Cr%Ti%
≤0,05≤1,00≤1,00≤0,4≤0,01516,0-18,0≤4x(C+N)+0,15

AISI 430 stainless steel offers protection from acidic environments and atmosphere.

C%Si%Mn%P%S%Cr%Ti%Nb%
≤0,03≤1,00≤1,00≤0,04≤0,0151,75-18,50,10-0,60≤3xC+0,3-1,00

Ferritic-magnetic stainless steel with the addition of Titanium and Niobium.

C%Si%Mn%P%S%Cr%Mo%N%Ti%
≤0,025≤1,0≤1,00≤0,04≤0,01517,0-20,01,80-2,50≤0,0304x(C+N)+0,15

Ferritic-magnetic stainless steel with the addition of Titanium and Molybdenum.